| PROPERTIES | EURO STANDARD EN-159/IS 13753 | OUR VALUE |
|---|---|---|
| DIMENSION & SURFACE QUALITY | ||
| Dimension | ± 0.5% | ± 0.2% |
| Deviation in Thickness | ± 0.6mm | ± 0.2mm |
| Straightness of sides | ± 0.3% | ± 0.2% |
| Rectangularity | ± 0.5% | ± 0.3% |
| Surface flatness | ± 0.5% | ± 0.3% |
| Surface Quality | Min 95% | Min 96% |
| PHYSICAL PROPERTIES | ||
| Water absorption | >10% | 13.5% |
| Bending Strength | > 150 Kg/Cm2 | 200-250 Kg/Cm2 |
| Scratch hardness (Mohs) | Min 3 | Min 3 |
| Crazing | 1 cycle | No Crazing at 5 Cycles |
| CHEMICAL PROPERTIES | ||
| Staining Resistance | Min Class 2 | Resistance to all Acids, Alkalies & Household Chemicals, except Hydro Fluoric Acid |
| Household Chemical | Min Class B | Resistance to all Acids, Alkalies & Household Chemicals, except Hydro Fluoric Acid |
| THERMAL PROPERTIES | ||
| Thermal Shock | Resistant to 10 Cycles | CONFORMS |
| Thermal Expansion | Max-9E-06 | CONFORMS |
GVT/PGVT Tiles
| PROPERTIES | ISO Standard 13006/EN 176 Group BIa | OUR VALUE |
|---|---|---|
| Length and width | ± 0.5% | ± 0.4% |
| Thickness | ± 5.0% | ± 3.0% |
| Straightness of sides | ± 0.5% | ± 0.5% |
| Rectangularity | ± 0.6% | ± 0.4% |
| Surface flatness | ± 0.5% | ± 0.2% |
| Water absorption | ± 3.6% | ± 3.6% |
| Breaking strength | ≥ 220 Kgs/cm2 | ≥ 270 Kgs/cm2 |
| Resistance to chemicals | resistance to all alkalis (except hydrochloric acid and its compound) | resistance to all alkalis (except hydrochloric acid and its compound) |
| Thermal shock | 10 cycles | 4 cycles |
Nano Tiles
| CHARACTERISTIC | STANDARD AS PER ISO-13006/ EN14411 GROUP Bla |
MEAN VALUE OF MAPS DOUBLE CHARGE VITRIFIED TILES |
TEST METHOD | |
| Regulatory Properties | Deviation In Length & Width | ± 0.5% | ± 0.10% | ISO-10545-2 |
| Deviation In Thickness | ± 5.00% | ± 2.00% | ISO-10545-2 | |
| Straightness of Sides | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Rectangularity | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Surface Flatness | ± 0.50% | ± 0.10% | ISO-10545-2 | |
| Color Differences | Unaltered | No Change | ISO-10545-16 | |
| Glossiness | As per Manufacture | Min.90 %* | Glossometer | |
| Surface Quality | Min.95% tiles should be free from visible defect |
Conforms | ISO 10545-2 | |
| Structural Properties | Water Absorption | ≤ 0.50 % | E ≤ 0.50% | ISO 10545-3 |
| Apparent Density | > 2.00 gm/cc | > 2.28 gm/cc | DIN 51082 | |
| Massive Mechanical Properties | Flexural Modulus Of Rupture | Min. 35N/mm² | Min. 40N/mm² | ISO-10545-4 |
| Flexural Breaking Strength | Min. 1300 N | Min. 2000 N | ISO-10545-4 | |
| Impact Resistance | As Per Manufacturer | Min. 0.55 | ISO-10545-5 | |
| Surface Mechanical Properties | Deep Abrasion Resistance | Max. 175mm³ | Max. 132mm³ | ISO-10545-6 |
| Moh's Hardnes | Min. 6 | ≥ 6 * | EN101 | |
| Thermo Hygrometric Properties | Frost Resistance | No. Damage | Frost Proof | ISO -10545-12 |
| Thermal Shock Resistance | No. Damage | No. Damage | ISO -10545-9 | |
| Moisture Expansion | Declared Value | Nil | ISO -10545-10 | |
| Thermal Expansion | Max.9.0 X 10-6 | Max. 6.5 X 10-6 | ISO -10545-8 | |
| Chemical Properties | Resistance of House Hold Chemical | No. Damage | No. Damage* | ISO -10545-13 |
| Stain Resistance | Resistance | Resistance* | ISO -10545-14 | |
| Safety Properties | Slip Resistance(friction Co Efficient) | >0.40 | >0.40 | ISO - 10545-17 |
Double Charge Tiles
| PROPERTIES | TEST METHOD | ISO STANDARD 13006 B1a TILES | OUR VALUE |
|---|---|---|---|
| Length and width | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Thickness | BS EN ISO 10545-2 | ± 5.0% | ± 3.0% |
| Straightness of sides | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Rectangularity | BS EN ISO 10545-2 | ± 0.6% | ± 0.3% |
| Surface flatness | BS EN ISO 10545-2 | ± 0.5% | ± 0.3% |
| Water absorption | BS EN ISO 10545-3 | ≤ 0.5% | ≤ 0.05% |
| Breaking strength | BS EN ISO 10545-4 | ≥ 1300N | ≥ 1500N |
| Modulus of rupture | BS EN ISO 10545-4 | ≥ 35 N/mm2 | ≥ 45 N/mm2 |
| Resistance to deep abrasion | BS EN ISO 10545-6 | ≤ 175mm3 | ≤ 150mm3 |
| Linear thermal expansion | BS EN ISO 10545-8 | ≤ 9 x 10-6 °C1 | ≤ 7 x 10-6 °C1 |
| Thermal shock resistance | BS EN ISO 10545-9 | No visible defect | No visible defect |
| Frost resistance | BS EN ISO 10545-12 | Frost proof | Frost proof |
| Resistance to chemicals | BS EN ISO 10545-13 | No visible effect | No visible effect |
| Resistance to stains | BS EN ISO 10545-14 |
Manufacturer to state class |
Stains removed
Min. Class 3 |
| Colour resistance | BS EN ISO 10545-16 | No damage | No damage |
| Colour resistance to UV Light | DIN 51094 | No change in color | No change in color |
| Scratch hardness (MOH's Scale) | EN 101 | ≥ 6 MOHS | ≥ 7 MOHS |
| Surface quality | BS EN ISO 10545-2 | Min. 95% | No visible defect |
| Skid resistance (friction co-efficient) | BS EN ISO 10545-17 | > 0.4 | > 0.4 |
| Moisture Expansion | - | Nil | Nil |
Porcelain Tiles
| 01 | Specific Weight | kg/dm3 | 2.35 - 2.45 |
|---|---|---|---|
| 02 | Water absorption (by weight) | % | <0.1 |
| 03 | Module of rupture | MPa | 36 - 65 |
| 04 | Compressive strength | MPa | 150 - 240 |
| 05 | Mohs hardness | grade | 6 -7 |
| 06 | Deep abrasion resistance | MM3 | ≤300 |
| 07 | Falling ball impact | 1000g ≥ 400 mm - 450g ≥ 800 mm | |
| 08 | Expansion coefficient | mm/oC | ≤ 3.5*105 |
| 09 | Temperature coefficent | - | 180oC environment resistance 24 hours |
| 10 | Dimensional stability | - | Class A |
| 11 | Surface slip resistance | - | Honed 400 polished |
| 12 | Acid chemical resistance | - | Resist |
| 13 | Suitability for kitchens | - | Suitable |